医用聚乙烯表面接枝2-甲基丙烯酰氧乙基磷酸胆碱对细菌生物膜形成的影响
Effect of MPC coating medical polyethylene surface on bacterial biofilm formation
-
摘要: 目的：探讨医用聚乙烯表面接枝2-甲基丙烯酰氧乙基磷酸胆碱（MPC）对金黄色葡萄球菌生物膜形成的影响。方法：利用紫外光接枝法将MPC接枝于医用聚乙烯薄片表面并用扫面电镜观察其表面形貌。以金黄色葡萄球菌（ATCC25923）标准菌株作为实验用菌，将已消毒的已接枝MPC聚乙烯薄片（观察组）及普通聚乙烯薄片（对照组）置入5 mL细菌浓度为1.5×107 cfu/mL的菌液中共同培养。分别于体外培养后24 h、48 h行膜内活菌计数和扫描电镜观察。结果：扫描电镜观察显示通过紫外光接枝法制备的MPC涂层聚乙烯薄片表面形貌光滑，原先的纹理消失。体外培养24 h、48 h观察组聚乙烯薄片表面活菌计数数量均显著少于对照组（P<0.01）；扫描电镜观察下进行细菌数半定量评估显示24 h、48 h观察组聚乙烯薄片表面细菌黏附量亦均少于对照组（P<0.01）。结论：医用聚乙烯表面接枝MPC可有效抑制细菌黏附，进而可预防聚乙烯表面细菌生物膜的形成。
-
关键词:
- 人工关节置换术 /
- 细菌生物膜 /
- 聚乙烯 /
- 2-甲基丙烯酰氧基乙基磷酰胆碱 /
- 金黄色葡萄球菌
Abstract: Objective: To explore the effects of medical polyethylene surface coated by 2-methacryloyloxy-ethyl phosphoric acid choline(MPC) on the formation of bacterial biofilm.Methods: The surface of medical polyethylene was coated with MPC using ultraviolet light grafting method,and its morphology was observed by scanning electron microscopy.The standard strain of Staphylococcus aureus(ATCC25923) was chose,and the polyethylene plate surface coated by MPC(observation group) and ordinary plate(control group) were co-cultured with 5 mL bacterial liquid(1.5×107 cfu/mL),respectively.After 24 h and 48 h of culturing,the viable bacteria adhered on the surface of plate in two groups were counted,and scanned by electron microscopy.Results: Scanning electron microscopy results showed that the medical polyethylene plate surface coated by MPC was smooth,the original texture of which disappeared.After 24 h and 48 h of culturing,the quantity of viable bacteria in observation group was significantly less than that in control group(P<0.05),and scanning electron microscopy results showed that the amount of adhesion bacterial of plate surface in observation group was significantly less than that in control group(P<0.05).Conclusions: MPC coating on medical polyethylene surface can effectively inhibit the bacterial adhesion,and prevent the bacterial biofilm formation. -
[1] DOBBINS CN.Bacterial colonization of orthopedic fixation devices in absence of clinical infection[J].J Infect Did,1998,158(1):203. [2] EPSTEIN AK,POKROY B,SEMINARA A,et al.Bacterial biofilm shows persistent resistance to liquid wetting and gas penetration[J].PNAS,2011,108(3):995. [3] DONLAN RM.Biofilm formation:a clinically relevant microbiological process[J].Clin Infect Dis,2001,38(8):1387. [4] SHIGETA M,TANAKA T,KOIKE N,et al.Suppression of fibroblast and bacterial adhesion by MPC coating on acrylic intraocular lenses[J].J Cat and Ref Sur,2006,32(5):859. [5] KAUR I,MISRA BN,KUMAR S.Graft copolymerization of methacrylic acid onto isotactic polypropylene by radiochemical methods[J].J Appl Polym Sci,1998,69(1):143. [6] BROWN MW,GIBERT P.Sensitivity of biofilm to antimicrobial agents[J].J Appl Bacterial,1993,74(Supp1):87. [7] GALLO J,KOLÁR M,FLORSCHVTZ AV,et al.In vitro testing of gentamicin-vancomycin losded bone cement to prewent prosthetic joint infection[J].Biomed Pap Fac Univ Palacky Olomouc Czech Repub,2005,149(1):153. [8] UFLNANUNTANA A,BONSIGNORE L,SHIRTLIF ME,et al.The effects of famesol on staphylococcus aureus biofilms and osteoblasts.An in vitro study[J].J Bone Joint Surg Am,2009,91(11):2683. [9] NAKAYA T,UMEDA T,IMOTO M.The convenient preparation of a vinyl monomer containing a phospholipid analogue[J].Makromol Chem Rapid Commun,1982,3(7):457. [10] ISHIHARA K,OSHIDA H,ENDO Y,et al.Hemocompatibility of human whole blood on polymers with a phospholipid polar group and its mechanism[J].J Biomed Mater Res,1992,26(12):1543. [11] HIROTA K,YUMOTO H,MIYAMOTO K,et al.MPC-polymer reduces adherence and biofilm formation by oral bacteria[J].J Dental Res,2011,90(7):900. [12] MACASSEY E,DAWES P.Biofilms and their role in otorhinolaryngological disease[J].J Laryngol Otol,2008,122(12):1273. [13] PUCKETT SD,TAYLOR E,RAIMONDO T,et al.The relationship between the nanostructure of titanium surfaces and bacterial attachment[J].Biomaterials,2010,31(4):706. -
点击查看大图
计量
- 文章访问数: 4118
- HTML全文浏览量: 526
- PDF下载量: 96
- 被引次数: 0
下载: